gap-fill depositions introducing hydroxyl-containing precursors in the formation of silicon containing dielectric materials

ABSTRACT

A chemical vapor deposition method for forming a dielectric material in a trench formed on a substrate. The method includes flowing a silicon-containing precursor into a process chamber housing the substrate, flowing an oxidizing gas into the chamber, and providing a hydroxyl-containing precursor in the process chamber. The method also includes reacting the silicon-containing precursor, oxidizing gas and hydroxyl-containing precursor to form the dielectric material in the trench. The ratio of the silicon-containing precursor to the oxidizing gas flowed into the chamber is increased over time to alter a rate of deposition of the dielectric material.

CROSS-REFERENCES TO RELATED APPLICATIONS

This application is a divisional of U.S. patent application Ser. No. 11/213,612, entitled “GAP-FILL DEPOSITIONS INTRODUCING HYDROXYL-CONTAINING PRECURSORS IN THE FORMATION OF SILICON CONTAINING DIELECTRIC MATERIALS,” filed Aug. 26, 2005, which claims the benefit of U.S. Provisional Application No. 60/605,116, filed Aug. 27, 2004, and entitled “GAP-FILL DEPOSITIONS INTRODUCING HYDROXYL-CONTAINING PRECURSORS IN THE FORMATION OF SILICON CONTAINING DIELECTRIC MATERIALS,” the entire contents of which are herein incorporated by this reference

BACKGROUND OF THE INVENTION

The fabrication sequence of integrated circuits often includes several patterning processes. The patterning processes may define a layer of conductors, such as a patterned metal or polysilicon layer, or may define isolation structures, such as trenches. In many cases the trenches are filled with an insulating, or dielectric, material. This insulating material can serve several functions. For example, in some applications the material serves to both electrically isolate one region of the IC from another, and electrically passivate the surface of the trench. The material also typically provides a base for the next layer of the semiconductor to be built upon.

After patterning a substrate, the patterned material is not flat. The topology of the pattern can interfere with or degrade subsequent wafer processing. It is often desirable to create a flat surface over the patterned material. Several methods have been developed to create such a flat, or “planarized”, surface. Examples include depositing a conformal layer of material of sufficient thickness and polishing the wafer to obtain a flat surface, depositing a conformal layer of material of sufficient thickness and etching the layer back to form a planarized surface, and forming a layer of relatively low-melting point material, such as doped silicon oxide, and then heating the wafer sufficiently to cause the doped silicon oxide to melt and flow as a liquid, resulting in a flat surface upon cooling. Each process has attributes that make that process desirable for a specific application.

As semiconductor design has advanced, the feature size of the semiconductor devices has dramatically decreased. Many circuits now have features, such as traces or trenches less than a micron across. While the reduction in feature size has allowed higher device density, more chips per wafer, more complex circuits, lower operating power consumption and lower cost among other benefits, the smaller geometries have also given rise to new problems, or have resurrected problems that were once solved for larger geometries.

An example of the type of manufacturing challenge presented by sub-micron devices is the ability to completely fill a narrow trench in a void-free manner. To fill a trench with silicon oxide, a layer of silicon oxide is first deposited on the patterned substrate. The silicon oxide layer typically covers the field, as well as walls and bottom of the trench. If the trench is wide and shallow, it is relatively easy to completely fill the trench. As the trench gets narrower and the aspect ratio (the ratio of the trench height to the trench width) increases, it becomes more likely that the opening of the trench will “pinch off”.

Pinching off a trench may trap a void within the trench. FIG. 1 shows such a void 4 formed in the dielectric material 2 that fills trench 1. These voids commonly occur in gapfill depositions where dielectric materials are rapidly deposited in high aspect ratio trenches. Void 4 creates inhomogeneities in the dielectric strength of the gapfill that can adversely affect the operation of a semiconductor device.

One approach to forming fewer voids is to slow down the dielectric deposition rate. Slower deposition rates facilitate a more conformal deposition of the dielectric material on the trench surfaces, which reduces excess buildup of dielectric materials on the top corners of the trench that can result in pinching off. As a result, trenches are more evenly filled from the bottom up. However, lowering the deposition rate of the dielectric material also reduces process efficiency by increasing the total dielectric deposition time. The slower dielectric deposition rates not only increase the time for filling trench 1, but also the bulk dielectric layer 3 on top of trench 1.

Another challenge encountered in gap-fill processes is the formation of weak seams at the interface of the dielectric material with a trench surface, as well as between surfaces of the dielectric materials itself. Weak seams can form when the deposited dielectric materials adhere weakly, or not at all, to the inside surfaces of a trench. Subsequent process steps (e.g., annealing) can detach the dielectric material from the trench surface and create a fissure in the gap-filled trench. Weak seams can also be formed between dielectric surfaces as illustrated in FIG. 2A, which shows a weak seam 9 in the middle of trench 5 that has been formed at the intersection of opposite faces of silicon oxide material 6 growing outward from opposite sidewalls (7 a and 7 b) of trench 5.

The dielectric material along seam 9 has a lower density and higher porosity than other portions of the dielectric material 6, which can cause an enhanced rate of etching along the seam 9. FIG. 2B illustrates how unwanted dishing 8 can develop along seam 4 when the dielectric material 6 is exposed to an etchant (e.g., HF) during processes such as chemical-mechanical polishing (CMP) and post-CMP cleaning. Like voids, weak seams create inhomogeneities in the dielectric strength of the gapfill that can adversely affect the operation of a semiconductor device.

In some circumstances, voids and weak seams in dielectric trench fills may be filled in or “healed” using a reflow process. For example, some doped silicon oxide dielectric materials experience viscous flow at elevated temperatures, permitting the reduction of voids and weak seams with high-temperature reflow processes. However, as the trench becomes narrower, it becomes more likely that the void will not be filled during these reflow process. In addition, reflow processes are not practical in many applications where high melting point dielectrics, such as undoped silicon oxide, are used for the gapfill. Thus, there remains a need for new systems and methods to reduce or eliminate voids and weak seams in dielectric gapfills.

BRIEF SUMMARY OF THE INVENTION

Embodiments of the invention include a chemical vapor deposition method for forming a dielectric material in a trench formed on a substrate. The method includes flowing a silicon-containing precursor into a process chamber housing the substrate, flowing an oxidizing gas into the chamber, and providing a hydroxyl-containing precursor in the process chamber. The method also includes reacting the silicon-containing precursor, oxidizing gas and hydroxyl-containing precursor to form the dielectric material in the trench. The ratio of the silicon-containing precursor to the oxidizing gas flowed into the chamber is increased over time to alter a rate of deposition of the dielectric material.

Embodiments of the invention also include a chemical vapor deposition method for forming a dielectric layer on a substrate. The method includes providing a silicon-containing precursor, an oxidizing processing gas, and a hydroxyl-containing precursor to a chamber housing the substrate. These precursors react to form the dielectric layer on the substrate. The ratio of the silicon-containing precursor to the oxidizing processing gas flowed into the chamber may be altered to change the deposition rate of the dielectric layer. The method may also include annealing the dielectric layer to increase a density of the dielectric layer.

Embodiments of the invention further include a substrate processing apparatus. The apparatus may include a substrate support configured to support a substrate within a processing chamber, and a gas delivery system configured to receive a silicon-containing precursor, a hydroxyl-containing precursor and an oxidizing processing gas and deliver them to the processing chamber. The apparatus may further include a controller configured to control the gas delivery system and the substrate support. The controller may introduce the silicon-containing precursor, the hydroxyl-containing precursor and oxidizing processing gas into the processor chamber to form a dielectric layer on the substrate, and alter the position of the substrate support relative to the gas delivery system during the deposition of the dielectric layer.

Additional embodiments and features are set forth in part in the description that follows, and in part will become apparent to those skilled in the art upon examination of the specification or may be learned by the practice of the invention. The features and advantages of the invention may be realized and attained by means of the instrumentalities, combinations, and methods described in the specification.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows a trench filled with a dielectric material that includes a void;

FIG. 2A shows a trench filled with a dielectric material that includes a weak seam;

FIG. 2B shows the conventional oxide-filled trench of FIG. 2A after a chemical mechanical polishing;

FIGS. 3A-B are flowcharts illustrating steps that may be included in processes of forming a dielectric layer on a substrate according to embodiments of the invention;

FIGS. 4A-B are simplified graphs plotting the relative concentration of a silicon-containing components over time according to embodiments of the invention;

FIGS. 5A-B are a set of comparative electron micrographs of gap-filled trenches;

FIGS. 6A-B are another set of comparative electron micrographs of gap-filled trenches;

FIG. 7 is a graph of dielectric film properties versus the flow rate of water vapor during the deposition of the dielectric film;

FIG. 8 shows a simplified cross-sectional view of an oxide-filled trench in accordance with an embodiment of the present invention;

FIG. 9 is a simplified cross section of a portion of an integrated circuit according to the present invention;

FIG. 10A is a simplified representation of a CVD apparatus according to the present invention;

FIG. 10B is a simplified representation of the user interface for a CVD system in relation to a deposition chamber in a multi-chamber system;

FIG. 10C is a simplified diagram of a gas panel and supply lines in relation to a deposition chamber; and

FIG. 10D shows a schematic view of another gas flow system in accordance with embodiments of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

As noted above, the development of voids and weak seams in trench isolations has become an increasing problem, particularly as trench widths get smaller (e.g., about 90 nm or less) and trench aspect ratios get higher (e.g., about 6:1 or higher). The present invention includes systems and methods of forming dielectric materials in these trenches using a hydroxyl-containing precursor (e.g., H₂O, hydrogen peroxide (H₂O₂), etc.) to help reduce voids and weak seams in the gapfill. The hydroxyl-containing precursor enhances the flowability and density of the silicon oxide material, helping to heal weak seams and fill in voids formed during the deposition.

Hydroxyl-containing precursors also increase the density of the silicon oxide material formed in the trench. The higher density of the material may provide advantages over less dense material, including giving the material a slower wet etch rate. Less dense materials deposited in the trenches by, for example, conventional, moisture free chemical vapor deposition typically have wet etch rates of about 5:1 or more. The high wet etch rates of the material can result in the overetching during subsequent planarization and/or oxide etching processes. This overetching may result in the formation of bowls or gaps at the tops of the trench isolations.

Embodiments of the invention include depositing the dielectric materials using high aspect ratio processes (HARPs). These processes include depositing the dielectric material at different rates in different stages of the process. For example, a lower deposition rate may be used to form a more conformal dielectric layer in a trench, while a higher deposition rate is used to form a bulk dielectric layer above the trench. In other examples, multiple rates (e.g., 3 or more rates) are used at various stages of the formation of the dielectric layer. Performing the deposition at a plurality of dielectric deposition rates reduces the number of voids and weak seams in the trenches without significantly reducing the efficiency of the deposition process. Combining the advantages of HARP with the enhanced flowability and higher density of dielectric materials formed with hydroxyl-containing precursors permits the efficient formation of low defect, high-density dielectric materials in trenches and bulk dielectric layers.

Exemplary Oxide Deposition Processes

FIG. 3A is a flowchart that illustrates steps that may be included in a process of forming a dielectric layer on a substrate according to embodiments of the invention. These embodiments include using HARP techniques for varying the deposition rate of the dielectric materials during the formation of the dielectric layer. The process includes providing a substrate in a process chamber at a first distance from the gas distribution manifold (e.g., showerhead) in step 302. The gas distribution manifold may include separate inlets for the precursor materials, or a single inlet through which mixtures of the precursors enter the process chamber.

After the substrate is placed in the process chamber, the precursor materials may flow through the manifold. This may include flowing an oxidizing gas precursor 306 (e.g., O₂, O₃, NO, NO₂, mixtures thereof, etc.), a silicon-containing precursor 308 (e.g., silane, dimethylsilane, trimethylsilane, tetramethylsilane, diethylsilane, tetramethylorthosilicate (TMOS), tetraethylorthosilicate (TEOS), octamethyltetrasiloxane (OMTS), octamethylcyclotetrasiloxane (OMCTS), tetramethylcyclotetrasiloxane (TOMCATS), mixtures thereof, etc.), and a hydroxyl-containing precursor 310 (e.g., H₂O, H₂O₂, etc.) through the manifold. Each precursor flows through the manifold and into the process chamber at an initial flow rate. For example, the silicon-containing precursor may initially flow through the manifold at about 20 to about 100 sccm, while the oxidizing precursor flows at about 60 to about 1000 sccm, and the hydroxyl-containing precursor flow at about 60 to about 200 sccm.

Depending on the type of CVD process used, the precursor materials may first help form a plasma whose products are used to form the dielectric layer on the substrate. Embodiments of the invention may be used with plasma CVD techniques such as plasma enhanced CVD (PECVD), and high density plasma CVD (HDPCVD), as well as thermal CVD techniques such as atmospheric pressure CVD (APCVD), sub-atmospheric CVD (SACVD), and low-pressure CVD (LPCVD), among others.

The initial flow rates of the precursors establish first flow rate ratios for the silicon-containing precursor:oxidizing gas precursor, and the silicon-containing precursor:hydroxyl-containing precursor. When the initial deposition of dielectric materials includes trench fills, the ratio of silicon-containing precursor:oxidizing gas precursor may be relatively low to provide a slower deposition of dielectric materials in the trenches. As the deposition progresses, the ratio of silicon-containing precursor:oxidizing gas precursor may be adjusted in step 312. For example, once a portion of the trenches has been filled, the ratio of silicon-containing precursor:oxidizing gas precursor may be increased to increase the deposition rate of the dielectric material. The adjustment is made at a stage of the deposition when there is reduced risk of the higher deposition rate causing voids or weak seams in the trenches.

The flow rate ratio of the silicon-containing precursor to the hydroxyl-containing precursor may also be relatively low in the initial deposition stage. When the flow rate ratio of silicon-containing precursor:oxidizing gas precursor is increased, the ratio of silicon-containing precursor:hydroxyl-containing precursor may increase as well. Alternatively, the ratio of silicon-containing precursor:hydroxyl-containing precursor may remain substantially constant as the ratio of silicon-containing precursor:oxidizing gas varies, such as embodiments where the silicon-containing and hydroxyl-containing precursors flow together into the process chamber.

FIG. 4A is a simplified graph plotting the concentration of a silicon-containing gas component relative to a process maximum, versus time, in an embodiment of a deposition process in accordance with the present invention featuring a stepped deposition rate profile. Alternative embodiments in accordance with the present invention could exhibit a wide variety of changing, non-linear composition profiles. FIG. 4B is a simplified graph plotting the concentration of a silicon-containing gas component relative to a process maximum, versus time, for another alternative embodiment of a deposition process in accordance with the present invention featuring a nonlinear profile.

Changes in composition of process gases flowed during the dielectric deposition may be accomplished in a variety of ways. Embodiments of the method have an increasing relative percentage of the silicon-containing precursor to the overall precursor mixture flow. Such an increase could be produced by elevating the flow rate of the silicon-containing precursor, reducing the flow rate of the oxidizing gas precursor, reducing the flow rate of the hydroxyl-containing precursor, or any combination of a change in flow rates of the components of the processing gas mixture which results in a change in the overall percentage composition of the silicon-containing precursor.

Moreover, a change in the relative ratio of components of the processing gas mixture may be accomplished by other than changing the flow rates of the components. For example, when ozone is used as the oxidizing gas precursor, it's frequently formed by flowing oxygen through an ozone generator, resulting in a gas flow comprising oxygen and some percentage of ozone. Changes in the concentration of silicon-containing precursor relative to ozone (i.e., the oxidizing gas precursor) could also be accomplished by altering the conditions of generation of the ozone to increase its concentration, without altering the flow rate of the ozone into the processing chamber.

The deposition rate of the dielectric layer may also be changed by adjusting the distance between the substrate and manifold to a second distance 314. The process chamber may include an adjustable lift that can vary the space between the substrate and the manifold during the deposition. As the substrate moves closer to the manifold, it enters a zone where the precursor materials are more concentrated, and form the dielectric layer at a faster rate. Thus, when the dielectric materials can be deposited on the substrate at a higher deposition rate without causing voids or weak seams, the substrate may be moved from an initial first distance to a second distance that is closer to the process chamber manifold.

At the completion of the deposition of the dielectric layer, the precursor materials stop flowing into the chamber 316. Additional process steps (e.g., annealing, chemical-mechanical polishing, etc.) may follow the dielectric deposition, before the substrate is removed from the process chamber.

Referring now to FIG. 3B, a flowchart illustrating steps for forming a dielectric layer on a substrate according to additional embodiments of the invention is shown. The process includes providing a substrate in a process chamber in step 301. The substrate is then heated in step 303 to a temperature at which the dielectric layer is formed (e.g., about 400° C. or more, about 450° C. to about 750° C., about 500° C. to about 600° C., etc.). Heating the substrate facilitates the chemical vapor deposition of precursor materials into solid, but flowable dielectric layer having a wet etch rate ratio (WERR) of about 2.5 or less. When the substrate is not heated, or heated to lower temperatures (e.g., about 200° C. or less), the deposited dielectric normally has a spin-on liquid consistency and has to undergo subsequent heating and/or annealing that can increase overall deposition time.

Precursor materials are provided to the heated substrate by flowing oxidizing gas precursor, silicon-containing precursor, and hydroxyl-containing precursor to the process chamber in steps 305, 306 and 307. The precursors may be mixed together and flow through a single channel into the process chamber at a constant flow rate until the flows are stopped at the end of the deposition 311. Alternatively, the silicon-containing precursor may flow though a channel that is independent of the oxidizing gas precursor and/or hydroxyl-containing precursor, and the flow rates of the precursors may be independently varied over the course of the deposition. The timing of the precursor materials may also be varied such that, for example, the oxidizing gas precursor and/or hydroxyl-containing precursor may be introduced before the silicon-containing precursor, or alternatively, all three precursors being introduced at the same time.

The dielectric layer formed on the substrate may be annealed in step 313. The anneal may be performed in the process chamber, or the substrate may be transferred to a separate annealing chamber. Exemplary anneal processes that may be used with embodiments of the invention will now be described.

Exemplary Post-Deposition Anneal Processes

Following the formation of the dielectric material, a post-deposition anneal may optionally be performed. The dielectric material may be annealed in an atmosphere such as N₂, N₂O, NO or NH₃. In one embodiment, the annealing process includes heating the substrate and flowing N₂O into the chamber or furnace. The N₂O interacts with the silicon oxide material at high temperatures and strengthens any remaining weak seams. The annealed layer is substantially seam-free and suited for further treatments such as CMP.

Annealing may take place in situ or ex situ. For example, the annealing may take place in the CVD chamber immediately after the deposition. Annealing alternatively may take place in another chamber of a multi-chamber system or in a different chamber system (e.g., a furnace). In some embodiments, annealing comprises a Rapid Thermal Process (RTP) as more fully described in U.S. Pat. No. 5,660,472, the entire disclosure of which is herein incorporated by reference for all purposes.

The annealing temperature may range from about 750° C. to about 1000° C. for furnace anneal and up to about 1200° C. for RTP anneal. The annealing duration is temperature dependent and may range from about 10 minutes to around 2 hours for furnace anneal and as few as 5 seconds up to around 3 minutes for RTP. As a result, in most cases, the layer is annealed by restructuring the SiO₂ network without exceeding the SiO₂ reflow temperature.

In other embodiments, the anneal process may include a multi-step anneal similar to those described in co-assigned U.S. Prov. Patent App. Ser. No. 60/598,939, titled “MULTISTEP ANNEAL OF THIN FILMS FOR FILM DENSIFICATION AND IMPROVED GAPFILL,” filed Aug. 4, 2004, by Nitin K. Ingle et al., the entire contents of which is hereby incorporated by reference for all purposes.

EXAMPLES

In these examples, silicon oxide (SiO₂) dielectric materials were deposited in substrate trenches using TEOS as the silicon-containing precursor, ozone as the oxidizing gas precursor and water vapor as the hydroxyl-containing precursor. The depositions are performed in a process chamber configured for thermal CVD.

Silicon oxide gap-fills were performed according to embodiments of the methods of the invention and comparative examples using conventional gap-fill techniques were also run. FIGS. 5A-B show electron micrographs of trenches filled with silicon oxide dielectric materials. The trenches had a width of about 0.15 μm and an aspect ratio (height/width) of about 6:1. FIG. 5A shows an electron micrograph of trenches filled with a silicon oxide dielectric using a conventional gap-fill technique. The conventional technique included a thermal CVD deposition at 540° C. using TEOS as the silicon-containing precursor flowing at about 5000 milligrams per minute (mgm). No hydroxyl-containing precursor is introduced during the deposition. An anneal is performed following the deposition for 30 minutes at 1050° C. in a nitrogen (N₂) atmosphere. The spots in the middle of the filled trenches and blurred lines around the edges of the trench in FIG. 5A show extensive formation of voids and weak seams.

In comparison, FIG. 5B shows an electron micrograph of trenches filled with a silicon oxide dielectric according to an embodiment of the methods of the present invention. During the deposition, 2500 mgm of H₂O was introduced with the TEOS. Other deposition conditions were substantially the same as for the conventional deposition described above for FIG. 5A. The micrograph in FIG. 5B lacks the spots and blurry trench edges indicative of the voids and weak seams seen in the gap-filled trenches of FIG. 5A.

Referring now to FIGS. 6A-B another pair of electron micrographs of trenches filled with silicon oxide dielectric materials are shown. Similar to FIGS. 6A-B, the trenches had a width of about 0.15 μm and an aspect ratio (height/width) of about 6:1. FIG. 6A shows an electron micrograph of trenches filled with a silicon oxide dielectric using a conventional gap-fill technique. The conventional technique included a thermal CVD deposition at 540° C. using TEOS as the silicon-containing precursor flowing at about 5000 milligrams per minute (mgm). The elongated spots in the middle of the filled trenches in FIG. 6A show extensive formation of voids.

In comparison, FIG. 6B shows an electron micrograph of trenches filled with a silicon oxide dielectric according to an embodiment of the methods of the present invention. During the deposition, 10 grams/minute of H₂O was introduced with the TEOS. Other deposition conditions were substantially the same as for the conventional deposition described above for FIG. 6A. The micrograph in FIG. 6B does not show any evidence of the elongated spots seen in FIG. 6A.

FIG. 7 shows a graph of the wet etch rate ratio (WERR) and percent shrinkage of the silicon oxide films as a function of water vapor flow rate (in grams/minute) during film deposition. The graph shows that the WERR decreases with increasing water vapor flow rate for depositions at both 850° C. and 1050° C. Also, the graph shows for the 850° C. deposition that there is a smaller % shrinkage following a post-deposition anneal as the water vapor flow rate increases. The drop in % shrinkage is particularly notable when going from a moisture-free deposition (i.e., 0 gm/min H₂O) to a deposition that includes some water vapor (i.e., 5 gm/min H₂O).

Exemplary Semiconductor Structure

FIG. 8 shows a simplified cross-sectional view of an oxide-filled trench structure formed utilizing an embodiment of a process in accordance with the present invention. Specifically, the time-varied flow rate ratio of silicon-containing precursor:oxidizing gas precursor during the deposition process results in formation of an oxide film 800 that includes a highly conformal portion 800 a proximate to the surrounding silicon sidewalls, but which also includes a less-conformal body portion 800 b which fills the entire volume of the trench 802 and creates overlying bulk layer 804 in a reasonable period of time. The oxide-filled trench 802 of FIG. 8 does not include the voids or weak seams associated with similar features formed utilizing the conventional oxide CVD processes previously described.

Trenches like the ones shown in FIG. 8 may be used in shallow trench isolation structures like those shown in FIG. 9, which illustrates simplified cross-section of an integrated circuit 200 according to embodiments of the invention. As shown in FIG. 9, the integrated circuit 200 includes NMOS and PMOS transistors 203 and 206, which are separated and electrically isolated from each other by oxide-filled trench isolation structure 220. Alternatively, field oxide isolation can be used to isolate devices, or a combination of isolation techniques may be used. Each of the transistors 203 and 206 comprises a source region 212, a gate region 215, and a drain region 218.

A premetal dielectric (PMD) layer 221 separates the transistors 203 and 206 from the metal layer 240, with connections between metal layer 240 and the transistors made by contacts 224. The premetal dielectric layer 221 may comprise a single layer or multiple layers. The metal layer 240 is one of four metal layers, 240, 242, 244, and 246, included in the integrated circuit 200. Each metal layer is separated from adjacent metal layers by intermetal dielectric layers 227, 228, and 229. Adjacent metal layers are connected at selected openings by vias 226. Planarized passivation layers 230 are deposited over the metal layer 246.

A silicon oxide layer according to the present invention may be used to form one or more of the dielectric layers shown in integrated circuit 200. For example, a silicon oxide layer deposited according to the present invention may be used to create trench isolation structure 220. A silicon oxide layer deposited according to the present invention may also be used to create PMD layer 221, or the higher layer intermetal dielectric layers 227-229 of the overlying interconnect structure.

A silicon oxide layer according to the present invention may also be used in damascene layers, which are included in some integrated circuits. In damascene layers, a blanket layer is deposited over a substrate, selectively etched through to the substrate, and then filled with metal and etched back or polished to form metal contacts 224. After the metal layer is deposited, a second blanket deposition is performed and selectively etched. The etched areas are then filled with metal and etched back or polished to form vias 226.

It should be understood that the simplified integrated circuit 200 is for illustrative purposes only. One of ordinary skill in the art could implement the present method for fabrication of other integrated circuits, such as microprocessors, application-specific integrated circuits (ASICs), memory devices, and the like.

Exemplary Deposition System

FIG. 10A is a simplified diagram of a chemical vapor deposition (“CVD”) system 10 according to embodiments of the invention. This system is suitable for performing thermal, sub-atmospheric CVD (“SACVD”) processes, as well as other processes, such as reflow, drive-in, cleaning, etching, and gettering processes. Multiple-step processes can also be performed on a single substrate or wafer without removing the substrate from the chamber. The major components of the system include, among others, a vacuum chamber 15 that receives process and other gases from a gas delivery system 89, a vacuum system 88, a remote microwave plasma system 55, and a control system 53. These and other components are described below in order to understand the present invention.

The CVD apparatus 10 includes an enclosure assembly 102 housing a vacuum chamber 15 with a gas reaction area 16. A gas distribution plate 20 is provided above the gas reaction area 16 for dispersing reactive gases and other gases, such as purge gases, through perforated holes in the gas distribution plate 20 to a wafer (not shown) that rests on a vertically movable heater 25 (also referred to as a wafer support pedestal). The heater 25 can be controllably moved between a lower position, where a wafer can be loaded or unloaded, for example, and a processing position closely adjacent to the gas distribution plate 20, indicated by a dashed line 13, or to other positions for other purposes, such as for an etch or cleaning process. A center board (not shown) includes sensors for providing information on the position of the wafer.

The heater 25 includes an electrically resistive heating element (not shown) enclosed in a ceramic. The ceramic protects the heating element from potentially corrosive chamber environments and allows the heater to attain temperatures up to about 800° C. In an exemplary embodiment, all surfaces of the heater 25 exposed to the vacuum chamber 15 are made of a ceramic material, such as aluminum oxide (Al₂O₃ or alumina) or aluminum nitride.

Reactive and carrier gases are supplied through the supply line 43 into a gas mixing box (also called a gas mixing block) 273, where they are preferably mixed together and delivered to the gas distribution plate 20. For example, silicon-containing precursor, such as silane, dimethylsilane, trimethylsilane, tetramethylsilane, diethylsilane, tetramethylorthosilicate (TMOS), tetraethylorthosilicate (TEOS), octamethyltetrasiloxane (OMTS), octamethylcyclotetrasiloxane (OMCTS), tetramethylcyclotetrasiloxane (TOMCATS), or mixtures thereof may be supplied to supply line 43 along with an oxide gas, such as oxygen (O₂), ozone (O₃), NO, NO₂, or mixtures thereof, and a hydroxyl-containing precursors such as H₂O, hydrogen peroxide, or mixtures thereof.

In alternate embodiments, the hydroxyl-containing precursor may be generated by combustion reactions that occur in (or near) vacuum chamber 15. For example, the hydroxyl-containing precursor may be in-situ generated steam (ISSG) that is generated by the combustion of hydrogen (H₂) and oxygen (O₂) in or near vacuum chamber 15 to form water vapor.

The gas mixing box 273 is preferably a dual input mixing block coupled to a process gas supply line 43 and to a cleaning/etch gas conduit 47. A valve 280 operates to admit or seal gas or plasma from the gas conduit 47 to the gas mixing block 273. The gas conduit 47 receives gases from an integral remote microwave plasma system 55, which has an inlet 57 for receiving input gases. During deposition processing, gas supplied to the plate 20 is vented toward the wafer surface (as indicated by arrows 21), where it may be uniformly distributed radially across the wafer surface, typically in a laminar flow.

Purging gas may be delivered into the vacuum chamber 15 from the plate 20 and/or an inlet port or tube (not shown) through the bottom wall of enclosure assembly 102. The purging gas flows upward from the inlet port past the heater 25 and to an annular pumping channel 40. An exhaust system then exhausts the gas (as indicated by arrows 22) into the annular pumping channel 40 and through an exhaust line 60 to a vacuum system 88, which includes a vacuum pump (not shown). Exhaust gases and entrained particles are drawn from the annular pumping channel 40 through the exhaust line 60 at a rate controlled by a throttle valve system 63.

In other embodiments (not shown) the silicon-containing precursors and the hydroxyl-containing precursors may travel through separate supply lines to a gas distribution plate in order to prevent them from reacting prematurely before reaching the substrate. As example of the dual channel supply line and showerhead design is described in co-assigned U.S. Pat. No. 6,624,091, titled “METHODS OF FORMING GAP FILL AND LAYERS FORMED THEREBY,” filed May 7, 2001, the entire contents of which is hereby incorporated by this reference for all purposes.

The remote microwave plasma system 55 can produce a plasma for selected applications, such as chamber cleaning or etching native oxide or residue from a process wafer. Plasma species produced in the remote plasma system 55 from precursors supplied via the input line 57 are sent via the conduit 47 for dispersion through the plate 20 to the vacuum chamber 15. Precursor gases for a cleaning application may include fluorine, chlorine, and other reactive elements. The remote microwave plasma system 55 also may be adapted to deposit plasma-enhanced CVD films by selecting appropriate deposition precursor gases for use in the remote microwave plasma system 55.

The system controller 53 controls activities and operating parameters of the deposition system. The processor 50 executes system control software, such as a computer program stored in a memory 70 coupled to the processor 50. Preferably, the memory 70 may be a hard disk drive, but of course the memory 70 may be other kinds of memory, such as read-only memory or flash memory. In addition to a hard disk drive (e.g., memory 70), the CVD apparatus 10 in a preferred embodiment includes a floppy disk drive and a card rack (not shown).

The processor 50 operates according to system control software, which includes sets of instructions that dictate the timing, mixture of gases, chamber pressure, chamber temperature, microwave power levels, susceptor position, and other parameters of a particular process. Other computer programs such as those stored on other memory including, for example, a floppy disk or another computer program product inserted in a disk drive or other appropriate drive, may also be used to operate the processor 50 to configure the CVD system 10 into various apparatus.

The processor 50 has a card rack (not shown) that contains a single-board computer, analog and digital input/output boards, interface boards and stepper motor controller boards. Various parts of the CVD system 10 conform to the Versa Modular European (VME) standard which defines board, card cage, and connector dimensions and types. The VME standard also defines the bus structure having a 16-bit data bus and 24-bit address bus.

FIG. 10B is a simplified diagram of a user interface in relation to the CVD apparatus chamber 30. The CVD apparatus 10 includes one chamber of a multichamber system. Wafers may be transferred from one chamber to another for additional processing. In some cases the wafers are transferred under vacuum or a selected gas. The interface between a user and the processor is via a CRT monitor 73 a and a light pen 73 b. A mainframe unit 75 provides electrical, plumbing, and other support functions for the CVD apparatus 10. Exemplary mainframe units compatible with the illustrative embodiment of the CVD apparatus are currently commercially available as the PRECISION 5000™, the CENTURA 5200™, and the PRODUCER SE™ systems from APPLIED MATERIALS, INC. of Santa Clara, Calif.

In the preferred embodiment two monitors 73 a are used, one mounted in the clean room wall 71 for the operators, and the other behind the wall 72 for the service technicians. Both monitors 73 a simultaneously display the same information, but only one light pen 73 b is enabled. The light pen 73 b detects light emitted by the CRT display with a light sensor in the tip of the pen. To select a particular screen or function, the operator touches a designated area of the display screen and pushes the button on the pen 73 b. The touched area changes its highlighted color, or a new menu or screen is displayed, confirming communication between the light pen and the display screen. Of course, other devices, such as a keyboard, mouse, or other pointing or communication device, may be used instead of or in addition to the light pen 73 b to allow the user to communicate with the processor.

FIG. 10C illustrates a general overview of an embodiment of the CVD apparatus 10 in relation to a gas supply panel 80 located in a clean room. As discussed above, the CVD system 10 includes a chamber 15 with a heater 25, a gas mixing box 273 with inputs from an inlet tube 43 and a conduit 47, and remote microwave plasma system 55 with input line 57. As mentioned above, the gas mixing box 273 is for mixing and injecting deposition gas(es) and clean gas(es) or other gas(es) through the inlet tube 43 to the processing chamber 15.

The remote microwave plasma system 55 is integrally located and mounted below the chamber 15 with the conduit 47 coming up alongside the chamber 15 to the gate valve 280 and the gas mixing box 273, located above the chamber 15. Microwave generator 110 and ozonator 115 are located remote from the clean room. Supply lines 83 and 85 from the gas supply panel 80 provide reactive gases to the gas supply line 43. The gas supply panel 80 includes lines from gas or liquid sources 90 that provide the process gases for the selected application. The gas supply panel 80 has a mixing system 93 that mixes selected gases before flow to the gas mixing box 273. In some embodiments, gas mixing system 93 includes a liquid injection system for vaporizing reactant liquids including silicon-containing precursors such as tetramethylorthosilicate (“TMOS”), tetraethylorthosilicate (“TEOS”), octamethyltetrasiloxane (OMTS), octamethylcyclotetrasiloxane (OMCTS), tetramethylcyclotetrasiloxane (TOMCATS), hydroxyl-containing precursors such as water, and hydrogen peroxide, and dopants such as triethylborate (“TEB”), triethylphosphate (“TEPO”) and diborane (B₂H₆). Vapor from the liquids is usually combined with a carrier gas, such as helium. Supply lines for the process gases may include (i) shut-off valves 95 that can be used to automatically or manually shut off the flow of process gas into line 85 or line 57, and (ii) liquid flow meters (LFM) 100 or other types of controllers that measure the flow of gas or liquid through the supply lines.

As an example, a mixture including TEOS as a silicon source may be used with gas mixing system 93 in a deposition process for forming a silicon oxide film. The TEPO is a liquid source that may be vaporized by conventional boiler-type or bubbler-type hot boxes. However, a liquid injection system is preferred as it provides greater control of the volume of reactant liquid introduced into the gas mixing system. The liquid is typically injected as a fine spray or mist into the carrier gas flow before being delivered to a heated gas delivery line 85 to the gas mixing block and chamber. One or more sources, such as oxygen (O₂), ozone (O₃), NO or NO₂ flow to the chamber through another gas delivery line 83, to be combined with the reactant gases from heated gas delivery line 85 near or in the chamber. Of course, it is recognized that other sources of dopants, silicon, and oxygen also may be used.

FIG. 10D is a simplified schematic diagram of a CVD deposition apparatus for depositing oxide layers in accordance with embodiments of the present invention. While the apparatus may be used to deposit silicon oxide films, it may also beneficially be applied to single- or multiple-layer doped silicon glass films, such as borophosphosilicate glass (“BPSG”), phosphosilicate glass (“PSG”), borosilicate glass (“BSG”), arsenic-silicon glass (“AsSG”), or similar films.

CVD deposition apparatus 400 comprises oxidizing gas source 416 and hydroxyl containing precursor source 417 in fluid communication with vacuum chamber 15 through gas mixing box 273. The oxidizing gas source 416 may contain oxygen (O₂), ozone (O₃), NO, NO₂, and mixtures of these gases, among other oxidizing gases. The hydroxyl containing precursor source 417 may contain H₂O, hydrogen peroxide (H₂O₂), and mixtures thereof, among other hydroxyl containing precursors. The hydroxyl containing precursors and oxidizing gases may be stored in sources 416 and 417 as liquids and/or gases.

Carrier gas source 410, silicon-containing gas source 411, first dopant gas (e.g., TEPO) source 412, and second dopant gas (e.g., TEB) source 413 are in fluid communication with vacuum chamber 15 through select valve 414 gas mixing system 93, and gas mixing box 273. Select valve 414 is selectively operable to shunt silicon- and dopant-containing gases such as TEOS vapor through divert line 402 to foreline 408 of chamber exhaust system 88, thereby circumventing vacuum chamber 15 entirely. Select valve 414 and divert line 402 allow the flow of silicon-containing gas to stabilize prior to its being routed to the vacuum chamber to commence an oxide CVD step in accordance with an embodiment of the present invention.

As noted above, the systems and methods of the invention may also be implemented on plasma based chemical vapor deposition systems. For example, the present invention may be used with plasma systems like the one described in commonly assigned U.S. Pat. No. 6,734,155, titled “PLASMA PROCESSES FOR DEPOSITING LOW DIELECTRIC CONSTANT FILMS,” filed Aug. 27, 2002, and HDP-CVD systems like the one described in commonly-assigned U.S. Pat. No. 6,740,601, titled “HDP-CVD DEPOSITION PROCESSES FOR FILLING HIGH ASPECT RATIO GAPS,” filed May 11, 2001, the entire contents of both patents being hereby incorporated by reference for all purposes.

While the above is a complete description of specific embodiments of the present invention, various modifications, variations, and alternatives may be employed. Alternative embodiments of process recipes in accordance with the present invention could call for flowing the silicon-containing component of the process gas flow at a sufficiently high initial concentration to allow the process gases to be introduced directly into the chamber, without an initial flow diversion phase.

Moreover, other techniques for varying the parameters of deposition of an oxide layer could be employed in conjunction with the variation in concentration of the process gas flow components described so far. Examples of other possible parameters to be varied include but are not limited to the temperature of deposition, the pressure of deposition, and the flow rate of processing gases containing dopants such as arsenic (As), boron (B), and phosphorous (P).

Having described several embodiments, it will be recognized by those of skill in the art that various modifications, alternative constructions, and equivalents may be used without departing from the spirit of the invention. Additionally, a number of well known processes and elements have not been described in order to avoid unnecessarily obscuring the present invention. Accordingly, the above description should not be taken as limiting the scope of the invention.

Where a range of values is provided, it is understood that each intervening value, to the tenth of the unit of the lower limit unless the context clearly dictates otherwise, between the upper and lower limits of that range is also specifically disclosed. Each smaller range between any stated value or intervening value in a stated range and any other stated or intervening value in that stated range is encompassed within the invention. The upper and lower limits of these smaller ranges may independently be included or excluded in the range, and each range where either, neither or both limits are included in the smaller ranges is also encompassed within the invention, subject to any specifically excluded limit in the stated range. Where the stated range includes one or both of the limits, ranges excluding either or both of those included limits are also included in the invention.

As used herein and in the appended claims, the singular forms “a”, “and”, and “the” include plural referents unless the context clearly dictates otherwise. Thus, for example, reference to “a process” includes a plurality of such processes and reference to “the electrode” includes reference to one or more electrodes and equivalents thereof known to those skilled in the art, and so forth.

Also, the words “comprise,” “comprising,” “include,” “including,” and “includes” when used in this specification and in the following claims are intended to specify the presence of stated features, integers, components, or steps, but they do not preclude the presence or addition of one or more other features, integers, components, steps, or groups. 

1. A substrate processing apparatus comprising: a substrate support configured to support a substrate within a processing chamber; a gas delivery system configured to receive a silicon-containing precursor, a hydroxyl-containing precursor and an oxidizing processing gas and deliver them to the processing chamber; and a controller configured to control the gas delivery system and the substrate support, wherein the controller introduces the silicon-containing precursor, the hydroxyl-containing precursor and oxidizing processing gas into the processor chamber to form a dielectric layer on the substrate, and alter the position of the substrate support relative to the gas delivery system during the deposition of the dielectric layer.
 2. The substrate processing chamber of claim 1, wherein the controller varies the concentration of the silicon-containing precursor to the oxidizing processing gas over time during the deposition of the dielectric layer on the substrate, as the silicon-containing precursor gas is continuously flowed into the chamber.
 3. The substrate processing chamber of claim 1, wherein the controller moves the substrate support closer to the gas delivery system during the deposition of the dielectric layer to increase a deposition rate for the dielectric layer.
 4. The substrate processing chamber of claim 1, wherein the gas delivery system comprises separate channels to deliver the silicon-containing precursor and the hydroxyl-containing precursor to the processing chamber.
 5. The substrate processing chamber of claim 1, wherein the silicon-containing precursor comprises tetraethylorthosilicate (TEOS), the hydroxyl-containing precursor comprises H₂O, and the oxidizing processing gas comprises ozone. 